|Weight:||25kgs||Application:||Welding,submerged Arc Welding, Steel Building,|
|Flux Content:||NO||Material:||Submerged ARC Welding|
Submerged ARC Welding flux and Welding wire F48A2 EM1K
Agglomerated flux type SJ301
Submerged ARC Welding wire H08MnA. / CHW-S12.
Flux / Wire Combination for Submerged Arc Welding Processing:
Executive Standards: AWS A5.17M F48A2-EM12K ;
IS0 14171-A-S 38 2 CS S2Si ;
IS0 14171-B-S 49A 2 CS SU21;
BS EN 756-S 38 2 CS S2Si ;
Type of Welding Flux: Agglomerated (sintered): Silicon calcium Neutral flux;
Type of Welding Current: DCEP or AC;
Features & Applications:
Agglomerated flux SJ301 is a silicon-calcium neutral sintered flux
and its basicity is about 1.0.
This combination is used for high speed welding structures made by mild steel
or equivalent tensile strength low alloy steels.
such as boilers and pressure vessels. It is suitable for large heat input welding of multi-layer welding, multi-pass welding as well as both sides multi-pass welding.
Chemical Composition (%)-(EM12K)
C: 0.05-0.15; Mn:0.80-1.25; Si:0.10-0.35;
S: ≤0.030;P: ≤0.030;Cr: —; Ni:—; Cu: ≤0.35;
Mechanical Properties of Deposited Metal (AW)
Tensile Strength Rm (MPa) : 480-660
Yield Strength ReL (MPa) : ≥400
Elongation A4 (%) : ≥22
Impact Value (J) -20℃ : ≥27
X-ray radiographic inspection: Grade Ⅰ;
Quality Guarantee of Flux:
Moisture: ≤0.10%; Solid Impurities :≤0.30%;
S: ≤0.060%; P: ≤0.080%;
Flux Mesh: 10-60;
To avoid rust the wire must be kept in dry condition and keep the package in good condition also before welding.
The flux should be re-baked at 300℃-350℃ for 1-2 hours before use.
The surfaces to be welded must be cleaned away impurities of oil contamination, rust, moisture and so on.
The welding conditions mentioned above for reference only and it is better to do a welding procedure qualification according to project before put it into formal welding.